s you may know, I use the Ultradent VALO curing light exclusively. It is a durable and highly robust tool. It offers three curing modes: standard at 1000 mW/cm2, High power at 1400 mW/cm2 and Xtra Po ... | |
![]() |
|
john kanca Replies: 3 Views: 1795 |
![]() |
John,
What are your thoughts about micro etching with 50 micron aluminum oxide prior to using Surpass. I've heard that micro etching increases bond strengths even more. What are your thoughts? S ... |
|
![]() |
|
john kanca Replies: 2 Views: 1746 |
![]() |
It would have been nice | |
![]() |
|
john kanca Replies: 0 Views: 1917 |
![]() |
I will once again be speaking at the Stars of Dentistry meeting in Hammersmith, London on June 15, 2018. Hope to see some of you there!
http://www.starsofdentistry.co.uk/ |
|
![]() |
|
john kanca Replies: 2 Views: 2151 |
![]() |
My understanding is to use interface as instructed, then I apply surpass 2, dry the snot out of it, light cure for 10 seconds and the crown is ready for bonding.
Josh Correct! |
|
![]() |
|
john kanca Replies: 3 Views: 1795 |
![]() |
John,
What are your thoughts about micro etching with 50 micron aluminum oxide prior to using Surpass. I've heard that micro etching increases bond strengths even more. What are your thoughts? S ... |
|
![]() |
|
john kanca Replies: 1 Views: 3283 |
![]() |
Golly, I apologize for missing this. Were you successful? | |
![]() |
|
john kanca Replies: 1 Views: 3313 |
![]() |
Can Superb be used with dual cures? Many of the single bond systems require and "activator" to use with a dual/chemical cure composite.
Yes it can |
|
![]() |
|
john kanca Replies: 1 Views: 2632 |
![]() |
It appears to be something really interesting but a ways from clinical use. I'll be interested to see whether this would be something one would insert as an indirect restoration or whether there would ... | |
![]() |
|
john kanca Replies: 3 Views: 2686 |
![]() |
It seems interesting for a few reasons, stronger tensile strength and release of desirables. Pedo operative, cervical lesions and small restoration under crown preps are the areas of consideration. ... | |
![]() |
|
john kanca Replies: 1 Views: 1484 |
![]() |
If it's me, I would apply some Surpass 2, dry it thoroughly and light-cure | |
![]() |
|
john kanca Replies: 3 Views: 2686 |
![]() |
Activa is resin modified glass ionomer with more resin than in the normal RMGI. I am not certain what role it fills as yet. It is not as wear resistant as filled resins. Nothing that dispenses and mi ... | |
![]() |
|
john kanca Replies: 1 Views: 1715 |
![]() |
Try the Titan White Opaque! ![]() |
|
![]() |
|
john kanca Replies: 1 Views: 2042 |
![]() |
Yes. Thin out Surpass 3 as much as you can. Then the excess will not be a problem. | |